ELEGOO ABS-Like 3D Printer Resin 3.0, 405nm UV-Curing Photopolymer Resin for Mars Saturn Jupiter MSLA DLP LCD 3D Printing with Strength and Toughness,

ELEGOO ABS-Like 3D Printer Resin 3.0, 405nm UV-Curing Photopolymer Resin for Mars Saturn Jupiter MSLA DLP LCD 3D Printing with Strength and Toughness,

【High Strength and Toughness】ELEGOO ABS-like resin 3.0 is engineered for high strength, impact resistance, and toughness. The printed models can withstand drilling holes and certain impacts, maintaining their structural integrity and resisting deformation, ideal for functional prototypes, mechanical parts, and industrial parts. 【High Precision & Low Shrinkage】With lower volume shrinkage, our ABS-like resin 3.0 ensures high precision in your 3D prints, resulting in intricate model details and smooth surface finishes with minimal distortion and accurate dimensional stability. 【Good Fluidity for Rapid Prototyping】ELEGOO ABS-like resin 3.0 is formulated with low viscosity to provide good fluidity for faster curing. Its viscosity is 25-47% lower than ABS-like 1.0, allowing the resin to quickly flow back into the print area and peel easily from the release film. This improves print success and reduces overall print time. 【Strong Stability】ELEGOO ABS-like resin 3.0 is engineered to maintain good stability, ensuring that the resin does not delaminate or separate over time. This eliminates the need for manual stirring and ensures consistent color across the model surface. 【Wide Compatibility】ELEGOO ABS-like resin 3.0 is compatible with a wide range of LCD/DLP 3D printers available on the market using 405nm UV light-curing technology, and works best with ELEGOO light-curing 3D printers. ABS Like 3.0 resin is a kind of upgraded formula resin. From the viscosity point of view, compared with ABS 1.0, the viscosity of ABS 3.0 is reduced by 25-47%, the success rate is higher, and the stability is stronger; in terms of elongation at break Look, compared to ABS 1.0, the elongation at break of ABS 3.0 is increased by 71%, the maximum bending strength is increased by 23.3%, and the impact strength is increased by 34%. While ensuring better toughness of the material, the deformation is smaller and the overall performance is better.
Parameter
Viscosity: 150-210mPa.s/25°C
Elongation at break: 24%
Maximum flexural strength: 50 MPa
Impact strength: 72.4 j/m
Packing specification: 500g, 1000g, 2kg